WUJIANG XINGHUA COMMUNICATION MATERIAL CO.,LTD

Professional manufacturer of water blocking materials for electric and optic cables

NON-CONDUCTIVE FOAM NONWOVEN FABRIC


 COMPOSITION:

- Polyester nonwoven fabric
- Polyester swelling powder


ZD20

PROPERTY
 TEST METHOD
 VALUE
 UNIT
Weight
  ISO 9037/1
  80 ± 10
  g/
 Thickness
  ISO 9037/2
  0.20 ± 0.03
  mm
 Tensile Strength
  ISO 9037/3
   ≥20
  n/cm
 Elongation
  ISO 9037/3
   ≥12
  %
 Swelling Speed
  Q/320584
   ≥5
  mm/1.min
 Swelling Height
  Q/320584
   ≥10
  mm/3.min
 Short Term Stability
  Q/320584
  230
   
 Long Term Stability
  IEC 216
  90
   
 Moisture Content (21,65%R.H.)
  Q/320584
  < 9
  %

* We can produce it according to customers requires, more details please contact us directly.

The figures above are tipical value and should not be used as the basic of specification.

ZD25

PROPERTY
 TEST METHOD
 VALUE
 UNIT
Weight
  ISO 9037/1
  90 ± 10
  g/
 Thickness
  ISO 9037/2
  0.25 ± 0.03
  mm
 Tensile Strength
  ISO 9037/3
   ≥30
 n/cm
 Elongation
  ISO 9037/3
   ≥12
  %
 Swelling Speed
  Q/320584
   ≥6
  mm/1.min
 Swelling Height
  Q/320584
   ≥12
  mm/3.min
 Short Term Stability
  Q/320584
  230
   
 Long Term Stability
  IEC 216
  90
   
 Moisture Content (21 ℃, 65%R.H.)
  Q/320584
  < 9
  %

* We can produce it according to customers requires, more details please contact us directly.

* The figures above are tipical value and should not be used as the basic of specification.

ZD30

PROPERTY
 TEST METHOD
 VALUE
 UNIT
Weight
 ISO 9037/1
  100 ± 10
  g/
 Thickness
 ISO 9037/2
  0.30 ± 0.03
  mm
 Tensile Strength
  ISO 9037/3
   ≥40
  n/cm
 Elongation
  ISO 9037/3
   ≥12
  %
 Swelling Speed
  Q/320584
   ≥8
  mm/1.min
 Swelling Height
  Q/320584
   ≥15
  mm/3.min
 Short Term Stability
  Q/320584
  230
   
 Long Term Stability
  IEC 216
  90
   
 Moisture Content (21 ℃, 65%R.H.)
  Q/320584
  < 9
  %

* We can produce it according to customers requires, more details please contact us directly.

* The figures above are tipical value and should not be used as the basic of specification.


SEMI-CONDUCTIVE FOAM NONWOVEN FABRIC


COMPOSITION:


     - Polyester nonwoven fabric

     - Polyacrylate swelling powder

     - Carbon black semi-conductive impregnation

BZD30

PROPERTY
 TEST METHOD
 VALUE
 UNIT
  Weight
  ISO 9037/1
  120 ± 10
  g / 
  Thickness
  ISO 9037/2
  0.30 ± 0.03
  mm
 Tensile Strength
  ISO 9037/3
     ≥30
  n/cm
  Elongation
 ISO 9037/3
     ≥12
 %
  Surface Resistance
  DIN 54345
  < 1500
  Ohm/ □
  Volume Resistance
  DIN 54345
  < 1 X 10^6
  Ohm.cm
  Swelling Speed
  Q/320584
    ≥8
  mm/1.min
  Swelling Height
  Q/320584
    ≥12
 mm/3.min
  Short Term Stability
  Q/320584
  230
   
  Long Term Stability
  IEC 216
  90
   
  Moisture Content (21 ℃, 65%R.H.)
  Q/320584
  < 9
  %

* We can produce it according to customers requires, more details please contact us directly.

* The figures above are tipical value and should not be used as the basic of specification.

BZD50

PROPERTY
 TEST METHOD
 VALUE
 UNIT
Weight
 ISO 9037/1
  160 ± 10
  g /
  Thickness
 ISO 9037/2
  0.50 ± 0.03
 mm
  Tensile Strength
  ISO 9037/3
   ≥40
  n/cm
  Elongation
  ISO 9037/3
   ≥12
  %
  Surface Resistance
  DIN 54345
  <1500
  Ohm/
  Volume Resistance
  DIN 54345
  <1 X 10^6
  Ohm.cm
  Swelling Speed
  Q/320584
   ≥10
  mm/1.min
  Swelling Height
  Q/320584
   ≥16
  mm/3.min
  Short Term Stability
  Q/320584
  230
   
  Long Term Stability
  IEC 216
  90
   
  Moisture Content (21 ℃, 65%R.H.)
  Q/320584
  < 9
  %

* We can produce it according to customers requires, more details please contact us directly.

* The figures above are tipical value and should not be used as the basic of specification.


SEMI-CONDUCTIVE NYLON TAPE INTRODUCTION


COMPOSITION:


        - Nylon fabric: Semi-conductive bonder

        - Shielding, binding between power cable

          components

        - No causticity

BNLD

 PROPERTY
 UNIT
 BNLD10
 BNLD12
 BNLD14
 MASS Per Unit Area
  g / 
  90 ± 10
  100 ± 10
  110 ± 10
  Thickness
  mm
  0.10 ± 0.02
  0.12 ± 0.02
  0.14 ± 0.02
  Tensile Strength
  N/cm
   ≥100
   ≥120
   ≥140
  Elongation
  %
   ≥25
   ≥25
   ≥25
  Surface Resistivity
   Ω
  <1000
  <1000
  <1000
  Volume Resistivity
   Ω.cm
  <1 X 10^5
  <1 X 10^5
  <1 X 10^5
  Short Term Stability
   
  230
  230
  230
  Long Term Stability
   
  145
  145
  145

* We can produce it according to customers requires, more details please contact us directly.

* The figures above are tipical value and should not be used as the basic of specification.


SEMI-CONDUCTIVE TETOLON TAPE INTRODUCTION


COMPOSITION:


        - Nylon fabric: Semi-conductive bonder

        - Shielding, binding between power cable

          components

        - No causticity

BTLD

PROPERTY
 UNIT
 BTLD18
 BTLD20
MASS Per Unit Area
  g / 
  130 ± 20
  170 ± 20
  Thickness
  mm
  0.18 ± 0.03
  0.20 ± 0.03
  Tensile Strength
  N/cm
   ≥150
   ≥230
  Elongation
  %
   ≥20
   ≥20
  Surface Resistivity
   Ω
  1000
  1000
  Volume Resistivity
   Ω.cm
  1 X 10^5
  1 X 10^5
  Short Term Stability
   
  230
  230
  Long Term Stability
   
  145
  145

* We can produce it according to customers requires, more details please contact us directly.

* The figures above are tipical value and should not be used as the basic of specification.


WATER BLOCKING YARN



COMPOSITION:



                - Polyester terylene long fiber


                - Polyacrylate super-absorbent resin

ZS

 PROPERTY
 UNIT
 ZS-0.5
 ZS-2.0
 ZS-3.0
 ZS-4.0
 ZS-5.0
 ZS-6.0
 Mass Per Length
  m/kg
 500 ± 50
 2000 ± 200
 3000 ± 300
 4000 ± 400
 5000 ± 500
 6000 ± 600
 Tensile Strength
  N
  ≥300
   ≥150
   ≥110
   ≥80
   ≥60
   ≥50
  Elongation
  %
  15
   ≥15
   ≥15
   ≥15
   ≥15
   ≥15
  Absorption Speed
  mm/g/1.min
  ≥50
   ≥50
   ≥45
   ≥40
   ≥35
   ≥30
  Absorption Capacity
  ml/g/5.min
  ≥60
   ≥60
   ≥55
   ≥50
   ≥45
   ≥40
  Short Term Stability
    
 230
  230
  230
  230
  230
  230
  Long Term Stability
   
 90
  90
  90
  90
  90
  90
  Moisture Content
  %
  ≤6
   ≤6
   ≤6
   ≤6
   ≤6
   ≤6

* We can produce it according to customers requires, more details please contact us directly.

* The figures above are tipical value and should not be used as the basic of specification.


NON-WOVEN TAPE




WFB10

PROPERTY
 TEST METHOD
 VALUE
 UNIT
Weight
ISO 9037/1
  50 ± 10
 g/ ㎡
Thickness
ISO 9037/2
  0.10 ± 0.03
  mm
Tensile Strength
ISO 9037/3
   ≥40
  n/cm
Elongation
ISO 9037/3
   ≥12
  %
Short Term Stability
Q/320584
  230
   
Long Term Stability
IEC 216
  90
   

* We can produce it according to customers requires, more details please contact us directly.

* The figures above are tipical value and should not be used as the basic of specification.


HIGHLY STRONG YARN ( Binding Yarns)






ZS1000D-3000D

 TYPE
 ZS1000D
1000D/192F
 ZS1500D
1500D/192F
 ZS3000D
3000D/384F
  Nominal Fineness - Denier
 1000 ± 25
  1500 ± 38
  3000 ± 75
  Nominal Finenese - Dtex
 1100 ± 27
  1670 ± 42
  3300 ± 82
  Breaking Strength (N)
   ≥75
   ≥107
   ≥225
  Tenacity - Denier
   ≥7.94
   ≥7.94
   ≥7.94
  Tenacity - Dtex
   ≥7
   ≥7
   ≥7
  Elongation at Break
  23.0 ± 2.0
  23.0 ± 2.0
  23.0 ± 2.0
  Shrinkage in Hot Air (%)
(177 ℃ x 10Min x 0.05cN/dtex Xpre-tension)
  4.8 ± 0.5
  4.8 ± 0.5
  4.8 ± 0.5

* We can produce it according to customers requires, more details please contact us directly.

* The figures above are tipical value and should not be used as the basic of specification.


Rip Cords




Polyester Rip Cord: SLS-P


Aramid Fiber Rip Cord: SLS-F

Polyester Rip Cord
Type
 SLS - P2.0
 SLS - P3.0
 SLS - P6.0
Nominal Fineness          ( Denier )
 2000  ±  25
  3000  ± 38
  6000  ± 125
Nominal Fineness          ( Dtex )
  2200
  3300
  6600
  Breaking Streagth ( N )
   ≥ 135
   ≥ 180
   ≥ 360
  Elongation ( % )
  10
  10
  10
  Water Content ( % )
  0.06
  0.06
  0.06
  Hot Air Shrinkage ( % )
177 ℃      2min      0.05 CN/Dtex
  7.0
  7.0
  7.0

* We can produce it according to customers requires, more details please contact us directly.

* The figures above are tipical value and should not be used as the basic of specification.

Aramid Fiber Rip Cord
 SLS - F2.0
 SLS - F3.0
 SLS - F4.0
Nominal Fineness
 2000 D
 3000 D
 4000 D
 Breaking Streagth ( N )
   ≥ 400
   ≥ 600
   ≥ 800
 Elongation ( % )
 0.5
 0.5
 0.5
 Water Content ( % )
 0.06
 0.06
 0.06
 Hot Air Shrinkage ( % )
                      177 ℃      2min      0.05 CN/Dtex
 0
 0
 0

* We can produce it according to customers requires, more details please contact us directly.

* The figures above are tipical value and should not be used as the basic of specification.